Versatile And Long-Lasting HDPE Geomenbrance For Anti-Seepage Applications
Product Introduction
HDPE geomembrane full name “High-density polyethylene geomembrane”,is a waterproof and barrier material made from high-density polyethylene resin. (geomembrane with a density of 0.94 g/cm3 or above) .
Product Properties
♦ excellent resistance to environmental stress cracking performance
♦ low temperature
♦ anti-aging
♦ corrosion resistance,
♦ as well as a larger service temperature range (-60-+ 60)
♦ a longer service life of 50 years
Product Application
It is widely used in the anti-seepage of domestic waste landfills, solid waste landfills, Sewage Treatment and artificial lakes, tailings treatment and other anti-seepage works.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark | |
| Item | |||||||||
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | ||
| Density (g/c㎡,≥) | 0.939 | ||||||||
| Tensile Properties | |||||||||
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | ||
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
| Yeild Elongation Rate (%) | 12 | ||||||||
| Breaking Elongation Rate (%) | 700 | ||||||||
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | ||
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | ||
| Environmental Stress Crack Resistance (h) (A single point of incision constant tensile method) |
300 | ||||||||
| Carbon Black | |||||||||
| Carbon Black Content(Rang) (%) | 2.0~3.0 | ||||||||
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 | ||||||||
| Oxidative Induction Time (OIT) | |||||||||
| Standard OIT (min) | 100 | ||||||||
| High Pressure OIT (min) | 400 | ||||||||
| 85℃ Oven Ageing (Minimum Average) | |||||||||
| 90 days after baking, the standard OIT retention(%) | 55 | ||||||||
| 90 days after baking, the hight pressure OIT retention(%) | 80 | ||||||||
| The Anti-UV Strength | |||||||||
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) | 50 | ||||||||
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) | 50 | ||||||||
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | ||||||||
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | ||||||||
| Dimensional Stability | ±2 | ||||||||
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
| Specification Item |
0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark | |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | ||
| Density (g/c㎡,≥) | 0.94 | ||||||||||
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | ||
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | ||
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |||||||
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | ||||||||||
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | ||
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | ||
| Carbon Black Content (%) | 2.0~3.0 | ||||||||||
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not allowed | ||||||||||