UV Resistant HDPE Smooth Geomembrane For Environmental Protection Projects
Product Introduction
Smooth geomembrane, also known as smooth geomembrane, is a widely used waterproof barrier geosynthetic material. The material is based on high polymer, adding carbon black, antioxidant, anti-aging agent, ultraviolet absorber and color masterbatch through special formula, and using three layer co-extrusion blow molding technology. Smooth geomemofilm has very low permeability, excellent chemical resistance and UV resistance characteristics, and has a very high cost performance, is the first choice of civil engineering project seepage prevention materials, widely used in water conservancy, environmental protection, municipal engineering, aquaculture, sewage treatment, tailings seepage prevention, landfill, landscape and water conservancy engineering and other fields.
Product Properties
Excellent water resistance and aging resistance.
Product Application
Smooth surface geomembrane can be used for seepage prevention, drainage and protection in water conservancy projects to improve the waterproof performance and stability of the project. In environmental protection projects, it can be used for seepage prevention and protection of landfill sites, sewage treatment plants and other places to reduce pollution to the environment. In the field of construction, it can be used for waterproof and protection of roofs, basements, swimming pools and other places to improve the service life and safety of buildings.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark | |
| Item | |||||||||
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | ||
| Density (g/c㎡,≥) | 0.939 | ||||||||
| Tensile Properties | |||||||||
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | ||
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
| Yeild Elongation Rate (%) | 12 | ||||||||
| Breaking Elongation Rate (%) | 700 | ||||||||
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | ||
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | ||
| Environmental Stress Crack Resistance (h) (A single point of incision constant tensile method) |
300 | ||||||||
| Carbon Black | |||||||||
| Carbon Black Content(Rang) (%) | 2.0~3.0 | ||||||||
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 | ||||||||
| Oxidative Induction Time (OIT) | |||||||||
| Standard OIT (min) | 100 | ||||||||
| High Pressure OIT (min) | 400 | ||||||||
| 85℃ Oven Ageing (Minimum Average) | |||||||||
| 90 days after baking, the standard OIT retention(%) | 55 | ||||||||
| 90 days after baking, the hight pressure OIT retention(%) | 80 | ||||||||
| The Anti-UV Strength | |||||||||
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) | 50 | ||||||||
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) | 50 | ||||||||
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | ||||||||
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | ||||||||
| Dimensional Stability | ±2 | ||||||||
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
| Specification Item |
0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark | |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | ||
| Density (g/c㎡,≥) | 0.94 | ||||||||||
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | ||
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | ||
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |||||||
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | ||||||||||
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | ||
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | ||
| Carbon Black Content (%) | 2.0~3.0 | ||||||||||
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not allowed | ||||||||||