Changsha Jian-Yi New Material Co., Ltd.
Make the project safer and the environment better!
Add to Cart
The HDPE Smooth Geomembrane is a strong and durable material that provides excellent protection against water leakage, chemicals, and other harmful substances. Its smooth surface ensures that it is easy to install and maintain, while also providing superior resistance against punctures and tears. This makes the HDPE Smooth Geomembrane ideal for use in harsh environments where other materials may not be able to withstand the conditions.
Smooth Surface
Excellent Waterproof Performance
Chemical Resistance
Ultraviolet Resistance
High mechanical strength
Easy Construction
Environmental Friendliness
Adaptability
For pond applications, the HDPE Smooth Pond Liner is a popular choice due to its durability and resistance to UV rays, chemicals, and punctures. It is easy to install and requires low maintenance, making it perfect for decorative ponds, fish ponds, and water gardens.
In the mining industry, the HDPE Smooth Geomembrane is an ideal solution for containing hazardous chemicals and waste materials. It provides a strong barrier against leakage and helps prevent environmental damage.
For landfill applications, the HDPE Smooth Geomembrane is crucial in preventing the contamination of soil and groundwater. It is a cost-effective solution that provides long-term protection for the environment.
In conclusion, the HDPE Smooth Geomembrane is a versatile product that has numerous applications in different industries. Its reliability, durability, and low maintenance make it a popular choice for customers.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark | |
| Item | |||||||||
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | ||
| Density (g/c㎡,≥) | 0.939 | ||||||||
| Tensile Properties | |||||||||
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | ||
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
| Yeild Elongation Rate (%) | 12 | ||||||||
| Breaking Elongation Rate (%) | 700 | ||||||||
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | ||
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | ||
| Environmental Stress Crack Resistance (h) (A single point of incision constant tensile method) |
300 | ||||||||
| Carbon Black | |||||||||
| Carbon Black Content(Rang) (%) | 2.0~3.0 | ||||||||
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 | ||||||||
| Oxidative Induction Time (OIT) | |||||||||
| Standard OIT (min) | 100 | ||||||||
| High Pressure OIT (min) | 400 | ||||||||
| 85℃ Oven Ageing (Minimum Average) | |||||||||
| 90 days after baking, the standard OIT retention(%) | 55 | ||||||||
| 90 days after baking, the hight pressure OIT retention(%) | 80 | ||||||||
| The Anti-UV Strength | |||||||||
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) | 50 | ||||||||
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) | 50 | ||||||||
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | ||||||||
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | ||||||||
| Dimensional Stability | ±2 | ||||||||
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
| Specification Item |
0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark | |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | ||
| Density (g/c㎡,≥) | 0.94 | ||||||||||
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | ||
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | ||
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |||||||
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | ||||||||||
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | ||
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | ||
| Carbon Black Content (%) | 2.0~3.0 | ||||||||||
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not allowed | ||||||||||